Bambu PLA Sparkle
Bambu PLA Sparkle is a next-level aesthetic filament that combines strength and sparkle. With metal particles included in its composition, Bambu PLA Sparkle adds a special sparkling look to your prints that sets them apart from the rest.
However, it is not recommended to use a 0.2 mm nozzle for printing as clogging may occur. Take your 3D printing projects to new heights with Bambu PLA Sparkle!
Display of PLA Sparkle Prints
Accessory Compatibility
Recommended | Not Recommended | |
Build Plate | Cool Plate SuperTack, Smooth PEI Plate, Textured PEI Plate | / |
Hotend | Hotend with Hardened Steel Nozzle 0.4 mm / 0.6 mm / 0.8 mm Hotend with Stainless Steel Nozzle 0.4 mm |
Hotend with Stainless Steel Nozzle 0.2 mm |
Glue | Bambu Liquid Glue Glue Stick |
/ |
PLA Sparkle Hex Code Table
Color | Hex Code | Display |
Classic Gold Sparkle | #CEA629 | |
Slate Gray Sparkle | #8E9089 | |
Crimson Red Sparkle | #792B36 | |
Royal Purple Sparkle | #483D8B | |
Alpine Green Sparkle | #3F5443 | |
Onyx Black Sparkle | #2D2B28 |
RFID for Intelligent Printing
All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System).
Load and print! No more tedious setting steps.
Recommended Printing Settings | |
Drying Settings (Blast Drying Oven) | 55 °C, 8 h |
Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
Nozzle Temperature | 190 - 230 °C |
Bed Temperature (with Glue) | 35 - 45 °C |
Printing Speed | < 250 mm/s |
Physical Properties | |
Density | 1.26 g/cm³ |
Vicat Softening Temperature | 57 °C |
Heat Deflection Temperature | 55 °C |
Melting Temperature | 156 °C |
Melt Index | 34.2 ± 3.3 g/10 min |
Mechanical Properties | |
Tensile Strength | 33 ± 3 MPa |
Breaking Elongation Rate | 11.7 ± 0.7 % |
Bending Modulus | 2310 ± 140 MPa |
Bending Strength | 63 ± 4 MPa |
Impact Strength | 66.5 ± 3.6 kJ/m² |